GRIP-O-MARK ™ ( PRODUCT DATA SHEET – CLAUSE 803.4 OF MORT & H)

  • Retro-Reflective Hot Melt Thermoplastic Road Marking Material with excellent whiteness .
  • Intermix glass beads offer long lasting retro-reflectivity.
  • Optimal balance between melt flow and flow resistance to achieve well-defined lines as per the desired width and thickness
  • Designed for tropical Indian conditions Excellent wear resistance and adhesion on asphalt roads.
  • Based on aliphatic chemistry; offers superior weathering resistance and color stability .
  • Suitable for application with manual or screed / extrusion automatic machines

    • TECHNICAL DATA

    Guiding Specification Clause No:803.4 of Ministry of Roads, Transport, and Highways
    Flow Resistance Not more than 25%
    Drying Not more than 15 mins.
    Binder Min 18 %
    Coat Thickness Min 2.5 mm
    Luminance Factor at 450 C as per AASHTO M249 White - 65% min,
    Yellow - 45% min
    Specific Gravity 1.9 to 2.0 kg/cc
    Skid Resistance > 45% as per BS 6044
    Glass Beads (Intermix) Min 30 % to Max 40%
    Finish Matt & Rough
    Ti O₂ (For White) Min 10%
    Packing 25 Kg Polylined Bag
    Fillers (For White) Max. 42%
    Storage Life Eighteen Months when stored in a cool, Dry place under the shed.

    Price & Other Features

    Prices INR 75.00/ kg to INR 85.00/ Kg
    Retro-Reflectivity in the Night 300 to 350 mcd/m²/ lux (High reflectivity guaranteed)
    Adhesion on bituminous surface Excellent wear resistance
    Specific Gravity 1.9 to 2.0 kg/cc
    Color Stability Presence to Rutile grade pigment possess long lasting colour stability .

    GRIP-O-MARK ™ ( PRODUCT DATA SHEET – B.S. )

  • Retro reflective Hot Melt Thermoplastic Road Marking Material with excellent whiteness .
  • Intermix glass beads offer long lasting retro reflectivity.
  • Optimal balance between melt flow and flow resistance to achieve well-defined lines as per the desired width and thickness.
  • Designed for tropical Indian conditions Excellent wear resistance and adhesion on asphalt roads.
  • Based on aliphatic chemistry; offers superior weathering resistance and color stability .
  • Suitable for application with manual or screed / extrusion automatic machines.

    • TECHNICAL DATA

    Guiding Specification Conforming to British Standards / Specification.(BS) 3262 : Part 1 / 1989
    Consistency Uniform Powder passing through 2.8 mm sieve 100 %
    Composition
  • Binder (Resin) = 20% ± 2%
  • Glass Beads (Intermix) = Min. 20 %
  • Aggregates including glass beads, pigment & extender = 80 ± 2%
    		•
    Flow Resistance Not more than 25%
    Drying
  • Surface Dry – within 15 mins.
  • Hard Dry – within 30 mins.
    		•
    Glass Beads (Intermix) 6088A (Type)
    Coat Thickness 2.5 mm (min)
    Luminance Factor at 450 C as per AASHTO M249
  • White >70%
  • Yellow >50%
    		•
    Skid Resistance > 45% as per BS 6044
    Finish Matt & Rough
    Packing 25 Kg Polylined Bag
    Storage Life Eighteen Months when stored in a cool, Dry place under the shed.

    GRIP-O-MARK ™
    (Concrete Adhesive Chemical Compound For Hot Melt Thermoplastic Road Marking on PQC /RCC Pavements )

    An effective solution used to improve the adhesion of thermoplastic road marking material on PQC surface.


    TECHNICAL DATA OF ADHESIVE COMPOUND FOR THERMOPLASTIC ROAD MARKING.

    S.No. Components Standards Required Actual Result
    1 Color Clear Clear
    2 Clarity Translucent Translucen
    3 Viscosity at 30 Degree as per Ford Cup No. 4 26 Sec. 26 Sec.
    4 Weight per Ltr. 0.96 kg/Ltr. 0.96 kg/Ltr.
    5 Volume Solids 33+-2% 31
    6 Drying Time at 30 degree Celsius 20 Min 11